SAE 1006 and SAE 1008 wires are also classified as low carbon steels. The parameters related to the hot rolling process for this group of wires are different from the previous samples due to their different chemical analysis and microstructure. The chemical analysis as well as the mechanical properties of these wires according to ASTM standard are presented in the table below. SAE 1006 and SAE 1008 wires are also classified as low carbon steels. The parameters related to the hot rolling process for this group of wires are different from the previous samples due to their different chemical analysis and microstructure. Chemical analysis as well as mechanical properties of these wires according to ASTM standard are presented in the table below.  

Steel grade	c	Mn	P	S	Si	Cr	UTS(MPa)	Elong	RA
SAE1006	0.08 MAX	0.25-0.4	MAX0.04	0.05MAX			360-450	37-45	65-75
SAE1008	0.1 MAX	0.3-0.5	MAX0.04	0.05 MAX			370-425	35-43	65-75

  RSt 34 and RSt 37 wires, which are in the category of low carbon steels, are produced in diameters of 5.5, 6.5 and 8 mm using hot rolling process. The main use of these wires in general applications such as structural applications O, packing wires, wires required for mesh and fence, production of nails, screws, rivets and…. Are offered to the market. The chemical composition of these products as well as their mechanical properties according to DIN standard are presented in the table below.

Steel grade	c	Mn	P	S	Si	Cr	UTS(MPa)	Elong	RA
RST34	0.11-0.16	0.5-0.8	MAX0.04	0.05MAX	0.04-0.07	0.01-0.014	360-420	38-45	67-78
RST37	0.12-0.18	0.6-0.8	MAX0.04	0.05 MAX	0.4-0.7	0.01-0.014	400-470	35-43	65-75